Morphology and Frictional Characteristics Under Electrical Currents of Al203/Cu Composites Prepared by Internal Oxidation

Two AhO3/Cu composites containing 0.24 wt.% A1203 and 0.60 wt.% A1203 separately are prepared by internal oxidation.Effectsof sliding speed and pressure on the fi-ictional characteristics of the composites and copper against brass are investigated and compared.The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope (SEM) and energy dispersive X-ray spectrum (EDS).The results show that the wear resistance of the AI203/Cu composites is superior to that of copperunder the same conditions.Under a given electrical current,the wear rate of AI203/Cu composites decreases as the AleO3-content increases.However,the wear rates of the Al203/Cu composites and copper increase as the sliding speed and pressure increase under drysliding condition.The main wear mechanisms for AleO3/Cu composites are of abrasion and adhesion;for copper,it is adhesion,although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.     

一种先进复合材料件无损检测的探讨

一种先进复合材料受力件的制品,如何检测内部是否有分层脱胶,曾遇到很大的困难。本文阐述如何结合实际解决这一难题,从而免受重大损失。     

多向层合板层间分层断裂韧性研究(英文)

在传统的柔度法和面积法的基础上 ,采用角度法对多向层合板层间分层断裂韧性进行了测试。该方法通过测量载荷与试验加载点处两子梁的夹角 ,不需要测量裂纹长度。同时对传统的柔度法进行了改进 ,改进后的柔度法可以用来测量两子梁刚度不等的 DCB试样。采用柔度法和角度法同时测试了碳纤维增强两种不同基体层合板 0 /θ(θ=0 ,30 ,6 0和 90°)层间分层断裂韧性 ,得出了分层断裂韧性随 θ的变化规律。这两种层合板分别为碳纤维增强脆性基体的 T30 0 / 4 2 1 1和碳纤维增强韧性基体的T30 0 / 32 6 1。结果发现 ,多向层合板层间分层断裂韧性与基体性能和分层界面处的铺层角有关     

复合材料面内剪切Iosipescue方法分析及试验研究

讨论了采用双Ｖ形开槽试样的Ｉｏｓｉｐｅｓｃｕ剪切试验方法的应用，分析了影响试验的因素，对Ｔ３００／５２２２复合材料单向板及π／４多向铺层层合板进行了试验研究。试验结果表明，此方法可以很好地用于复合材料剪切试验。     

轻质量低成本无人机舵面结构优化与验证

复合材料蜂窝夹芯结构因其高比强度、比模量及可设计性而广泛应用于航空飞行器结构。文章提出了 1种轻质量、低成本舵面结构方案——通过增大蜂窝芯密度使其剪切模量提高,进而降低复合材料面板应力水平,减小面板厚度。首先,根据理论选择通过增大蜂窝密度提升蜂窝剪切模量;然后,对结构进行有限元计算与分析,发现蒙皮应力水平随蜂窝芯剪切模量增大而显著降低;最后,设计不同蜂窝芯密度的蜂窝夹芯结构进行试验。试验结果证明,蜂窝芯越致密,其典型力学性能越高,冲击后的剩余强度也越高。     

2.5维编织树脂基复合材料平板多尺度动力学模型修正

在2.5维编织树脂基复合材料多尺度固有振动分析的基础上,开展基于实测结构模态数据的复合材料平板动力学模型修正研究,以获取精准反映其动力学特性的模型。首先,建立复合材料平板固有频率对弹性参数的灵敏度分析方法,分析了平板固有振动特性的主要影响因素;其次,建立基于灵敏度分析的复合材料多尺度动力学模型修正方法,形成了基于MSC.NASTRAN平台的模型修正程序。最后,利用实测结构模态测试数据,实现对复合材料平板动力学模型的修正。结果表明,对关键弹性参数进行修正后,不同边界条件和纱线走向的复合材料平板试验件固有频率实测数据与仿真数据的最大误差由10.44%下降至2.39%,相关性得到了大幅改善。此外,所提出的自由模态测试方案结合动力学模型修正方法,为复合材料等效弹性参数的试验辨识提供了新的技术途径。     

Stability analysis of robotic longitudinal-torsional composite ultrasonic milling

Currently, industrial robots are considered as an alternative towards traditional machine tools. Especially for the large-scale parts milling, robotic flexibility and low cost make it possess the irreplaceability. However, the milling chatter caused by its weak rigidity hampers robotic application and promotion severely in aviation industry. Rotary ultrasonic milling (RUM) technology with one-dimensional axial vibration has been proven and approved on avoiding robotic chatter. Based on this, the research of project team demonstrates that longitudinal-torsional composite ultrasonic milling (CUM-LT) involving separation characteristic has a greater advantage than RUM in terms of chatter suppression. Thereby, the CUM-LT as a new means is applied to avoid processing vibration of robotic milling system. And its influence mechanism on stability improvement of weak stiffness processing system is clarified. Meanwhile, the approaches to strengthen separation effect are provided innovatively. Moreover, a new analysis method of robotic CUM-LT (RCUM-LT) stability is proposed on the basis of ultrasonic function angles. The simulation and experimental results indicate that compared with robotic RUM (RRUM), stability regions of separated RCUM-LT (SRCUM-LT) and unseparated RCUM-LT (URCUM-LT) are improved by 124.42% and 39.20%, respectively. The addition of torsional ultrasonic energy has a wonderful effect on the milling chatter suppression of low stiffness robots.     

三维五向编织复合材料的冲击压缩特性及破坏机制

利用分离式霍普金森压杆(split Hopkinson pressure bar,SHPB)实验系统和高速摄像技术对三维五向碳/环氧编织复合材料的动态压缩特性进行研究。通过对编织角为22.3°的试样分别进行沿纵向和横向方向的冲击压缩实验,得到材料在200~1200 s^-1应变率范围内的应力应变曲线,并结合高速摄像记录的动态压缩过程,对不同应变率下材料在高速变形下的渐进破坏规律进行分析。同时,综合试样的宏观破坏特征和微观断口形貌特征,进一步分析材料的破坏模式及破坏机理。结果表明:随着应变率的增加,材料在纵向和横向均具有一定的应变率强化效应,在横向方向的应变率强化效应更为显著;不同加载方向下材料的渐进破坏过程、应力应变曲线特征以及破坏方式均具有明显差异,且随着应变率的增加而发生改变。     

硫化压力对橡胶／金属热硫化粘接剥离强度的影响

研究 NR1155天然橡胶在不同硫化压力下热硫化后的物理力学性能。基于90°粘合剥离强度测试方法分别测量了不同硫化压力下制备的橡胶／金属复合结构试样的粘合剥离强度,并采用低场 NMR 橡胶交联密度测定仪分析试样中橡胶部分的交联密度,同时采用冷场发射电子扫描显微镜（SEM）研究剥离破坏表面。结果表明：NR1155天然橡胶胶料与 Chemlok205／Chemlok220热硫化胶粘体系具有很好的相容性和协同硫化作用。随着硫化压力的提高,橡胶／金属的粘合剥离强度呈现先降低后增加的规律,且最大剥离力呈现对硫化压力的函数依赖关系,而硫化胶的交联密度则呈现相反的趋势。